polyvinyl chloride (PVC) flashing Tape
T&P PVC waterproof flashing tape:
1)UV rays resistance
2)long service life
3)aging resistance
Features:
1)Exposed to sunshine: UV rays resistance, long service life and aging resistance
2)Easy installation and dimensional stability: can be wieldable under wide range of temperature and experience minus dimensional change in thermal treatment
3)3 meters width reduce the joints and help saving materials or labor cost
4)Good flexibility under low temperature, good adaptability to ambient temperature difference
5)Good plasticity: convenient and fast treatment of detailed parts of corners and edges
6)High tensile strength and elongation thus can accommodate movements of substrates
7)Secure anti-puncture and good rooting resistance, no pollution caused to environment when being welded and good waterproofing choice for plant roofs
Long Lige Fire Resistance Root and Resistance Elasticity
UV-Resistance Hot Air Welding Chemical Resistance Tensile Strengt
Available size:
Thickness(mm) | Width(mm) | Length(m) |
1.2 | 100/150/200 | 15 or 20/roll |
1.5 | 100/150/200 | 15 or 20/roll |
2.0 | 100/150/200 | 15 or 20/roll |
Note: Other sizes can be offered upon specific requirements | ||
Specification:
No. | ITEM | I | II | |
1 | Tension strength / Mpa | 8.0 | 12.0 | |
2 | Fracture elongation ≥ / % | 200 | 250 | |
3 | Measurement changing at heating / % | 3.0 | 2.0 | |
4 | Cold bending | -20°C no leaking | -25°C no leaking | |
5 | Perforation resistance | Water impermeability | ||
6 | Water impermeabvilitv | Water impermeability | ||
7 | Binding property with cutting(N/mm) | Appearance | 3.0/breaking membrane | |
8 | Hot air ageing | Appearance | No craze,nobubble,nocohering,hole | |
Tension strength / % | ±25 | ±20 | ||
Fracture elongation changing rate | ||||
Cold bending / % | -15°C no leaking | -20°C no leaking | ||
9 | Chemistry corrosion resistance | Tension strength / % | ±25 | ±20 |
Fracture elongation changing rate | ||||
Cold bending / % | -15°C no leaking | -20°C no leaking | ||
10 | Phytotrons acceleratingageing | Tension strength / % | ±25 | ±20 |
Fracture elongation changing rate | ||||
Cold bending / % | -20°C no leaking | -20°C no leaking | ||